PA6 Ultramid B2703
PA6 Ultramid B27E01
PA6 Ultramid B27E
PA6 Ultramid B27SD02
PA6 Ultramid B27SD05
PA6 Ultramid B29HM01
PA6 Ultramid B3201
PA6 Ultramid B32
PA6 Ultramid B3301
PA6 Ultramid B33L01
PA6 Ultramid B33L
PA6 Ultramid B33LN01
PA6 Ultramid B35EG3
PA6 Ultramid B35G3 BK00564
PA6 Ultramid B35G3 SI BK23216
PA6 Ultramid B3601
PA6 Ultramid B36LN01
PA6 Ultramid B36LN
PA6 Ultramid B36
PA6 Ultramid B3EG10
PA6 Ultramid B3EG2
PA6 Ultramid B3EG3
PA6 Ultramid B3EG4
PA6 Ultramid B3EG5
PA6 Ultramid B3EG6
PA6 Ultramid B3EG7
PA6 Ultramid B3EG10SI
PA6 Ultramid B3G8
PA6 Ultramid B3GK24
PA6 Ultramid B3GM35
PA6 Ultramid B3K
PA6 Ultramid B3L
PA6 Ultramid B3M6
PA6 Ultramid B3S BK00464
PA6 Ultramid B3S HP
PA6 Ultramid B3S Q661
PA6 Ultramid B3S
PA6 Ultramid B3U Q721
PA6 Ultramid B3UG4
PA6 Ultramid B3UGM210
PA6 Ultramid B3UM4
PA6 Ultramid B3WG10 BK00564
PA6 Ultramid B3WG10 BK564
PA6 Ultramid B3WG3
PA6 Ultramid B3WG5
PA6 Ultramid B3WG6
PA6 Ultramid B3WG7
PA6 Ultramid B3WG8 BK00564
PA6 Ultramid B3WGM24
成型性能:
1.结晶料,熔点较高熔融温度范围窄,热稳定性差,料温超过300度,滞留时间超过30min即分解。较易吸湿,需干燥,含水量不得超过0.3%。
2.流动性好,易溢料。宜用自锁时喷嘴,并应加热。
3.成型收缩范围及收缩率大,方向性明显,易发生缩孔,变形等。
4.模温按塑件壁厚在20-90度范围内选取,注射压力按注射机类型,料温,塑件形状尺寸,模具浇注系统选定,成型周期按塑件壁厚选定。树脂粘度小时,注射,冷却时间应取长,并用白油作脱模剂。
5.模具浇注系统的形式和尺寸,增大流道和浇口尺寸可减少缩水。
特性:
1、优良的力学性能。尼龙的机械强度高,韧性好。
2、自润性、耐摩擦性好。尼龙有良好的自润性,摩擦系数小,作为传动部件其使用寿命长。
3、优良的耐热性。如PA46等高结晶性尼龙的热变形温度很高,可在150°C下长期使用。PA66经过玻璃纤维增强以后,其热变形温度达到250°C以上。
4、的电绝缘性能。尼龙的体积电阻很高,耐击穿电压高,是优良的电气、电器绝缘材料。
5、优良的耐气候性。
6、吸水性。尼龙的吸水性大,饱和水可达到3%以上。在一定程度影响制件的尺寸稳定性。
PA66的收缩率为0.8%——1.3%,烘料 80°烘4小时,料筒温度250°——270°,模温90°,熔点260°-280°。